Modèle: A588 GR.A/ GR.B
La Norme: AiSi, ASTM, bs, VACARME, GB, JIS
Lieu D'origine: Chine
Espèce: Plaque d'acier
Processus De Production: Laminé à chaud
Application: Plaque de chaudière, Plaque de conteneur, Plaque de navire
Acier Spécial: Acier résistant à l'usure, Plaque d'acier à haute résistance
Tolérance: ± 1%
Catégorie: Plaque faiblement alliée, Plaque d'acier pour navire, Plaque de cuve de chaudière, Feuille d'acier laminée à chaud
Service De Traitement: Pliant, Soudage, Décollage, Coupe, Perforation
Détails d'emballage: Emballage marin standard, ou comme l'exige le client
productivité: 10000 Tons Per Month
transport: Ocean,Land,Express
Soutenir: 10000 Tons Per Month
Certificats : ISO 9001
Hafen: Qingdao,Tianjin,Shanghai
Type de paiement: L/C,T/T,D/P
Incoterm: FOB,CFR,CIF,EXW
Plage de stock:
Norme: ASTM A588 Grade A, grade B, grade K
Plage d'épaisseur: 5 - 150 mm
Plage de largeur: 900 - 4800 mm
Plage de longueurs: 3000 - 12000 mm
Services de coupe en acier: acier de découpe de flammes, acier au laser, tôle en acier de coupe à jet, découpe de plasma
ASTM A588 Grade A, B est la spécification pour la structure de la corrosion atmosphérique l'acier de structure de haute résistance à faible alliage et la limite d'élasticité minimum 50 KSI 345 MPa. Il couvre le matériau de grade A, de grade B et de grade K comprend des formes en acier, des plaques et des barres pour la construction soudée, rivetée ou boulonnée, mais est destinée principalement à une utilisation dans les ponts et les bâtiments soudés où des économies de poids ou une durabilité supplémentaire sont importantes.
Les principales classes en acier résistantes à la corrosion atmosphérique sont: Corten A, Corten B; ASTM A588; ASTM A242; EN10025-5 EN10155 S235J0W, S235J2W, S355J0WP, S355J2WP, S355J0W; TBT1979 09CUPCRNI-A, 05CUPCRNI, GBT4171 Q355GNH, Q235NH, Q295NH, Q355NH; JIS G3125 Spa-H, Spa-C; et ainsi de suite .
Normes ASTM:
Spécifications A6 / A6M pour les exigences générales pour les barres, plaques, formes et empilage de feuille de structure roulée
Guide G101 pour estimer la résistance à la corrosion atmosphérique des aciers à faible alliage
Les produits structurels fournis en vertu de la présente spécification doivent être conformes aux exigences de l'édition actuelle de la spécification A6 / A6M, pour le produit structurel spécifique ordonné, à moins qu'un conflit existe, auquel cas cette spécification prévaudra.
Les bobines sont exclues de la qualification à cette spécification jusqu'à ce qu'elles soient transformées dans un produit structurel fini. Cela signifie que les produits ont été coupés à des longueurs individuelles d'une bobine.
L'acier doit être conçu en pratique des grains fines.
ASTM A588 Grade A, ASTM A588 Grade B, ASTM A588 Grade K.
|
A588/A588M TABLE1 Chemical Requirements (Heat Analysis) |
|||
|
|
Composition,% |
||
|
Element |
Grade A |
Grade B |
Grade K |
|
Carbon ① |
0.19 max |
0.20 max |
0.17 max |
|
Manganese ① |
0.80-1.25 |
0.75-1.35 |
0.50-1.20 |
|
Phosphorus ③ |
0.030 max |
0.030 max |
0.030 max |
|
Sulfur ③ |
0.030 max |
0.030 max |
0.030 max |
|
Silicon |
0.30-0.65 |
0.15-0.50 |
0.25-0.50 |
|
Nickel |
0.40 max |
0.50 max |
0.40 max |
|
Chromium |
0.40-0.65 |
0.40-0.70 |
0.40-0.70 |
|
Molybdenum |
|
|
0.10 max |
|
Copper |
0.25-0.40 |
0.20-0.40 |
0.30-0.50 |
|
Vanadium |
0.02-0.10 |
0.01-0.10 |
|
|
Columbium |
|
|
0.005-0.05 ② |
|
① For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50%. ② For plates under in.[13 mm] in thickness, the minimum columbium is waived. ③ A maximum phosphorus content of 0.04% and a maximum sulfur content of 0.05% are permitted for the following materials. .Structural shapes .Bars .Plates with widths up to and including 15 in. [380 mm] |
|||
|
A588/A588M TABLE2 Tensile Requirements ① |
||||
|
NoTE I-Where"..."appears in this table, there is no requirement |
||||
|
|
|
Plates and Bars |
|
Structural Shapes |
|
For Thicknesses |
For Thicknesses |
For Thicknesses |
All |
|
|
4 in.[100mm] and Under |
Over 4 in.[100mm] to 5 in.[125mm] incl |
Over 5 in.[125mm] to 8 in.[200mm] incl |
||
|
Tensile strength,min,ksi [MPa] |
70[485] |
67[460] |
63[435] |
70[485] |
|
Yield point,min,ksi [MPa] |
50[345] |
46[315] |
42[290] |
50[345] |
|
Elongation in 8in.[200 mm].min.% |
18 ②③ |
... |
... |
18 ③ |
|
Elongation in 2 in.[50 mm].min,% |
21 ②③ |
21 ②③ |
21 ②③ |
21 ④ |
|
① See specimen orientation under the Tension Tests section of Specification A6/A6M. ② Elongation not required to be determined for floor plate. ③ For plates wider than 24 in. [600mm], the elongation requirement is reduced two percentage points. See elongation requirement adjustments in the Tension Tests section of Specification A6/A6M. ④ For wide flange shapes with flange thickness over 3 in. (75mm), elongation in 2in.[50mm] of 18% minimum applies. |
||||
Les exigences supplémentaires ne s'appliquent que si elles sont spécifiées dans l'ordonnance ou le contrat. Les exigences supplémentaires standardisées pour une utilisation à l'option de l'acheteur sont répertoriées dans les spécifications A6 / A6M. Ceux qui sont considérés comme adaptés à une utilisation avec cette spécification sont répertoriés:
S2. Analyse du produit
S3. Traitement thermique simulé post-soudage des coupons de test mécanique.
S5. Test d'impact Charpy V-norch
S6. Test de poids drop pour le matériau 0,625 en 16 mm et plus en épaisseur.
S8. Examen à ultrasons.
S15. Réducion de la mesure de la zone.
S18. Résistance à la traction maximale
S30. Test d'impact en V Charpy pour les formes structurelles alternatives de l'emplacement du noyau et
S32. Paquets de chaleur unique
La plaque A242 est un acier structurel à faible alliage avec des économies de poids et une résistance à la corrosion atmosphérique.
À partir de la composition chimique ASTM A242, un contenu inférieur de carbone, de phosphore et de soufre, il n'a qu'un seul type et A588 a trois types, A588 Grade A, B, K.
La plaque ASTM A588 de grade A équivaut à Corten une plaque d'acier. La plaque ASTM A242 est équivalente à Corten B. Par rapport à l'acier à faible résistance à faible alliage commun tel que A572 Grade 50, ASTM A588 et ASTM A242 présente des avantages de performances résistantes à l'altération.
En un mot ASTM A588 couvre plus de gammes d'acier d'altération que A242.
Notre gamme d'approvisionnement
Norme: ASTM A588 Grade A, grade B, grade K
Plage d'épaisseur: 5 - 150 mm
Plage de largeur: 900 - 4800 mm
Plage de longueurs: 3000 - 12000 mm